Fine Sand Texture Powder Coating for Aluminum and Furnitures Jxz01

Basic Info

Model NO.	JXZ01
Substrate	Steel & Aluminum & Metal
Components	Pigment
Formation Mechanism	Conversion Type
Powder Coating	Rough Texture Powder Coating
Transport Package	PP Bag + Carton Box
Specification	20KG/25KG/Carton
Trademark	KINNO
Origin	China
Production Capacity	10000tons/Year

Product Description

Metalic Paints And Powder Coatings System

Types	Item No.	RatioPE/Crosslinker	Viscosity(p/200ºC)/mpa.s	Tg Value(°C)	Coating film thickness(um)	Curing conditions
Matter Series Powder Coating	JX01	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min
Smooth Matte Series Powder Coating	JP01	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min
Smooth Glossy Series Powder Coating	JG01	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min
Metallic Matte Series Powder Coating	JX01	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min
Metallic Fine Texture Matte Series Powder Coating	JS01	93/7	4800~6000	≥65	40um~80um	160°C/20min;180°C/15min ;200°C/12min
Metallic Rough Texture Glossy Series Powder Coating	JZ01	93/7	4800~6000	≥65	40um~80um	160°C/20min;180°C/15min ;200°C/12min
Smooth Flat Matte Series Powder Coating	JF01	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min

Fine Sand Texture Powder Coating for Aluminum and Furnitures Jxz01

Product Description

Fine Sand Texture Powder Coating for Aluminum and Furnitures Jxz01

Physical And Chemical Properties
Rough coating film thickness	40um~80um
Curing conditions	160°C/20min; 180°C/15min; 200°C/12min
Acid value	30-35mgkOH/g
Glass transition temperature	≥65
Viscosity (200 ° C,mpa.s)	4800-6000mPa.s/200°C
Indentation hardness	≥80
Adhesion	Grade 0
Impact resistance	no cracking
Cupping test	6mm without cracking
Bending resistance	3mm without cracking
Chemical stability	no bubbles, softening, falling off
Salt spray corrosion resistance	R≤9.5
Moisture and heat resistance	≤ grade 1
Artificially accelerated weather resistance	level 0
Boiling water resistance	no bubbles, water spots, wrinkle spinning, falling off, slightly color difference allowed
Preparation method	After mixing the prepared polyester resin with curing agent TGIC, pigments, fillers and auxiliary agents according to the formula ratio, melt extrusion, tablet pressing and crushing with a twin-screw extruder, and then pulverize the sheet material and sieve it to make it. powder coating. It is sprayed on the surface-treated metal plate with an electrostatic spray gun.

Foshan Faxus New Material Company Limited

Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties.

STORAGE CONDITION